Nano tape

Nano tape, also called gecko tape; marketed under the name Alien Tape, is a synthetic adhesive tape consisting of arrays of carbon nanotubes transferred onto a backing material of flexible polymer tape. These arrays are called synthetic setae and mimic the nanostructures found on the toes of a gecko; this is an example of biomimicry. The adhesion is achieved not with chemical adhesives, but via van der Waals forces, which are weak electric forces generated between two atoms or molecules that are very close to each other.

Explanation

Geckos show a remarkable ability to climb smooth vertical surfaces at high speeds, exhibiting both strong attachment and easy rapid removal, or shear adhesion, of their feet.

On a gecko's foot, micrometer-sized elastic hairs called setae are split into nanometer-sized structures called spatulas. The shear adhesion is achieved by forming and breaking van der Waals forces between these microscopic structures and the substrate.

Nano tapes mimic these structures with carbon nanotube bundles, which simulate setae, and individual nanotubes, which simulate spatulas, to achieve macroscopic shear adhesion and to translate the weak van der Waals interactions into high shear forces. The shear adhesion allows the tape to be easily peeled off, in the manner a gecko lifts its foot; and since the carbon nanotube arrays leave no residue on the substrate, the tape can be reused many times.

History

Nano tape is one of the first developments of synthetic setae, which arose from a collaboration between the Manchester Centre for Mesoscience and Nanotechnology, and the Institute for Microelectronics Technology in Russia. Work started in 2001 and two years later results were published in ''Nature Materials''. Geim, A.K., Dubonos, S.V., Grigorieva, I.V., Novoselov, K.S., Zhukov, A.A. and Shapoval, S.Y. (2003), "Microfabricated adhesive mimicking gecko foot-hair", ''Nature Materials'', v.2, pp.461–3

The group prepared flexible fibers of polyimide as the synthetic setae structures on the surface of a 5 μm thick film of the same material using electron beam lithography and dry etching in an oxygen plasma. The fibres were 2 μm long, with a diameter of around 500 nm and a periodicity of 1.6 μm, and covered an area of roughly 1 cm² (see figure on the left). Initially, the team used a silicon wafer as a substrate, but found that the tape's adhesive power increased by almost 1,000 times if they used a soft bonding substrate such as Scotch tape. This is because the flexible substrate yields a much higher ratio of the number of setae in contact with the surface over the total number of setae.

The result of this "gecko tape" was tested by attaching a sample to the hand of a 15 cm high plastic Spider-Man figure weighing 40 g, which enabled it to stick to a glass ceiling, as is shown in the figure. The tape, which had a contact area of around 0.5 cm² with the glass, was able to carry a load of more than 100 g. However, the adhesion coefficient was only 0.06, which is low compared with real geckos (8~16).

Commercial use

Commercial nano tape is usually sold as double-sided tape that is useful for hanging lightweight items such as pictures and decorative items on smooth walls without punching holes in the wall. Using superaligned carbon nanotubes, some nano tapes can stay sticky in extreme temperatures.

Gallery

Gecko Leaftail 1.jpg, Gecko climbing a glass surface
Gecko foot on glass.JPG, Close view of a gecko's foot
Micro and nano view of gecko's toe.jpg, Micro and nano view of gecko's toe
Micro view of Gecko Tape.jpg, Micro view of nano tape
Test of gecko tape.jpg, "Spider-Man test" of nano tape

References

{{Reflist

Adhesive tape
Biophysics
Biomimetics
Nanotechnology
Carbon nanotubes
Emerging technologies