Precipitation strengthening
Extracted from the Wikipedia article Precipitation hardening.
Alloy design
Precipitation strengthening is possible if the line of solid solubility slopes strongly toward the center of a phase diagram. While a large volume of precipitate particles is desirable, a small enough amount of the alloying element should be added so that it remains easily soluble at some reasonable annealing temperature. Although large volumes are often wanted, they are wanted in small particle sizes as to avoid a decrease in strength as is explained below.