Williams–Landel–Ferry Equation

The Williams– Landel– Ferry Equation (or WLF Equation) is an empirical equation associated with time–temperature superposition.

The WLF equation has the form
: $\log(a_T) = \frac$
where ''$\log(a_T)$'' is the decadic logarithm of the WLF shift factor, ''T'' is the temperature, ''T''_r is a reference temperature chosen to construct the compliance master curve and ''C''₁, ''C''₂ are empirical constants adjusted to fit the values of the superposition parameter ''a''_T.

The equation can be used to fit (regress) discrete values of the shift factor a_T vs. temperature. Here, values of shift factor a_T are obtained by horizontal shift log(a_T) of creep compliance data plotted vs. time or frequency in double logarithmic scale so that a data set obtained experimentally at temperature T superposes with the data set at temperature T_r. A minimum of three values of a_T are needed to obtain C₁, C₂, and typically more than three are used.

Once constructed, the WLF equation allows for the estimation of the temperature shift factor for temperatures other than those for which the material was tested. In this way, the master curve can be applied to other temperatures. However, when the constants are obtained with data at temperatures above the glass transition temperature (T_g), the WLF equation is applicable to temperatures at or above T_g only; the constants are positive and represent Arrhenius behavior. Extrapolation to temperatures below T_g is erroneous. When the constants are obtained with data at temperatures below T_g, negative values of C₁, C₂ are obtained, which are not applicable above T_g and do not represent Arrhenius behavior. Therefore, the constants obtained above T_g are not useful for predicting the response of the polymer for structural applications, which necessarily must operate at temperatures below T_g.

The WLF equation is a consequence of time–temperature superposition (TTSP), which mathematically is an application of
Boltzmann's superposition principle. It is TTSP, not WLF, that allows the assembly of a compliance master curve that spans more time, or frequency, than afforded by the time available for experimentation or the frequency range of the instrumentation, such as dynamic mechanical analyzer (DMA).

While the time span of a TTSP master curve is broad, according to Struik,L. C. E. Struik, Physical aging in amorphous polymers and other materials, Elsevier Scientific Pub. Co. ; New York, 1978. it is valid only if the data sets did not suffer from ageing effects during the test time. Even then, the master curve represents a hypothetical material that does not age. Effective Time Theory. needs to be used to obtain useful prediction for long term time.E. J. Barbero, Time–temperature–age superposition principle for predicting long-term response of linear viscoelastic materials, chapter 2 in Creep and fatigue in polymer matrix composites, R. M. Guedes, editor, Woodhead Pub. Co., UK, 2010.

Having data above T_g, it is possible to predict the behavior (compliance, storage modulus, etc.) of viscoelastic materials for temperatures T>T_g, and/or for times/frequencies longer/slower than the time available for experimentation. With the master curve and associated WLF equation it is possible to predict the mechanical properties of the polymer out of time scale of the machine (typically $10^$ to $10^2$ Hz), thus extrapolating the results of multi-frequency analysis to a broader range, out of measurement range of machine.

Predicting the Effect of Temperature on Viscosity by the WLF Equation

The Williams-Landel-Ferry model, or WLF for short, is usually used for polymer melts or other fluids that have a glass transition temperature.

The model is:

:$\mu(T)\,=\,\mu_0 10^ \left( \frac \right)$

where ''T''-temperature, $C_1$, $C_2$, $T_r$ and $\mu_0$ are empiric parameters (only three of them are independent from each other).

If one selects the parameter $T_r$ based on the glass transition temperature, then the parameters $C_1$, $C_2$ become very similar for the wide class of polymers. Typically, if $T_r$ is set to match the glass transition temperature $T_g$, we get

:$C_1 \approx$17.44

and

:$C_2 \approx 51.6$ K.

Van Krevelen recommends to choose

:$T_r\,=\,T_g+43$ K, then

:$C_1 \approx 8.86$

and

:$C_2 \approx$101.6 K.

Using such ''universal parameters'' allows one to guess the temperature dependence of a polymer by knowing the viscosity at a single temperature.

In reality the ''universal parameters'' are not that universal, and it is much better to fit the WLF parameters to the experimental data, within the temperature range of interest.

Further reading

* Williams-Landel-Ferry model
* Time–temperature superposition
*Viscoelasticity